PBT 2016 CELANESE USA
CELANEX®
Electrical field,Electronic field,Laptop case
Processability,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/2016 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | 55 KJ/m |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 4.8 KJ/m |
| Flexural modulus | 23℃ | ISO 178 | 3100 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 4.5 KJ/m |
| -30℃ | ISO 179/1eA | 4.5 KJ/m | |
| Impact strength of simply supported beam without notch | -30℃ | ISO 179/1eU | 55 KJ/m |
| Tensile modulus | 1mm/min | ISO 527-2/1A | 3000 Mpa |
| Tensile stress | 50mm/min，屈服 | ISO 527-2/1A | 60 Mpa |
| Tensile modulus | 50mm/min，屈服 | ISO 527-2/1A | 3 % |
| Rockwell hardness | ISO 2039-2 | 79 M | |
| bending strength | 23℃ | ISO 178 | 95 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/2016 |
|---|---|---|---|
| Volume resistivity | 1MHz | IEC 06250 | 3.5 |
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| Dielectric dissipation factor | 100Hz | IEC 60250 | 47 E-4 |
| 1MHz | IEC 60250 | 185 E-4 | |
| Volume resistivity | 100Hz | IEC 60250 | 3.6 |
| Surface Resistivity | IEC 60093 | 1E+15 Ohm | |
| Volume resistivity | IEC 60093 | 1E+13 ohm.m |
| physical property | Test Condition | Test Method | CELANESE USA/2016 |
|---|---|---|---|
| Water absorption rate | 23℃,50%相对湿度 | ISO 62 | 0.2 % |
| Melt volume flow rate | ISO 1133 | 18 CM | |
| Water absorption rate | 23℃,饱和 | ISO 62 | 0.45 % |
| Shrinkage rate | 纵向 | ISO 294-4 | 1.2-1.6 % |
| density | ISO 1183 | 1440 kg/m |
| Thermal performance | Test Condition | Test Method | CELANESE USA/2016 |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-1 | 60 °C | |
| Limiting Oxygen Index | ISO 4589 | 30 % | |
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 60 °C |
| 0.45Mpa，HDT | ISO 75-1/-2 | 165 °C | |
| vicat | ISO 306 | 190 °C | |
| melting temperature | ISO 11357-1 | 225 °C | |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 0.77 E-4/℃ |
| 纵向 | ISO 11359-2 | 0.63 E-4/℃ | |
| UL flame retardant rating | UL 94 | V-0 |