Impact strength of simply supported beam without notch
-30°C
ISO 179/2U
80 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/2U
无断裂
-30°C
ASTM D256
36 J/m
0°C
ASTM D256
36 J/m
23°C
ASTM D256
38 J/m
-30°C
ISO 180/1A
4.0 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
--2
ASTM D638
2500 Mpa
yield
ASTM D638
60.0 Mpa
yield
ISO 527-2/50
60.0 Mpa
crack
ASTM D638
60.0 Mpa
crack
ISO 527-2/50
60.0 Mpa
yield
ASTM D638
7.0 %
yield
ISO 527-2/50
10 %
crack
ASTM D638
15 %
crack
ISO 527-2/50
15 %
Bending modulus
ISO 178
2400 Mpa
bending strength
ISO 178
85.0 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
0.45MPa, unannealed, 64.0mm span
ISO 75-2/Bf
150 °C
1.8MPa, unannealed, 64.0mm span of
ISO 75-2/Af
50.0 °C
Ball Pressure Test
125°C
IEC 60695-10-2
Pass
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Melt Volume Flow Rate (MVR)
250°C/2.16kg
ISO 1133
20.0 cm3/10min
Melt Volume Flow Rate (MVR)
250°C/5.0kg
ISO 1133
50.0 cm3/10min
Shrinkage rate
MD
Internal Method
2.0-2.6 %
Shrinkage rate
TD
Internal Method
0.90-1.8 %
Water absorption rate
Saturation,23°C
ISO 62
0.34 %
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
0.080 %
hardness
شرایط آزمون
روش آزمون
نتیجه آزمون
Rockwell hardness
R-Sale
ISO 2039-2
117
Ball Pressure Test
H358/30
ISO 2039-1
145 Mpa