physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	250°C/1.0kg	ISO 1133	8.7 g/10min
Melt volume flow rate	250°C/2.16kg	ISO 1133	16.0 cm3/10min
Viscosity value	0.5%OCP	内部方法	1.23 cm³/g

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength		ISO 527-1/-2	58 MPa
bending strength		ISO 178	83 MPa
Flexural modulus		ISO 178	2.4 Gpa
Charpy Notched Impact Strength		ISO 179/1eA	5.1 KJ/m
Flexural modulus		ISO 178	2400 Mpa
bending strength		ASTM D790	82.0 Mpa
bending strength	bending strength		ISO 178	83.0 Mpa
tensile strength	屈服	ASTM D638	54.0 Mpa
tensile strength	tensile strength		ISO 527-2	58.0 Mpa
elongation	断裂	ASTM D638	>150 %
Tensile strain	断裂	ISO 527-2	120 %
Flexural modulus		ASTM D790	2500 Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	5.1 kg·cm/cm(J/M)ft·lb/in
elongation at break		ASTM D638/ISO 527	120 %
tensile strength		ASTM D638/ISO 527	58 kg/cm²(MPa)[Lb/in²]
Flexural modulus		ASTM D790/ISO 178	2.4 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	83 kg/cm²(MPa)[Lb/in²]

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792/ISO 1183	1.315
melt mass-flow rate		ASTM D1238/ISO 1133	224 g/10min

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating		UL94	HB
melting temperature			224 °C