Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1200M TORAY JAPAN
Toraycon®
Bottle cap,Electric wire,Cable,Food service sector
transparent,standard
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1200M |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 83 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2.4 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790 | 82.0 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 5.1 KJ/m | |
| elongation at break | ASTM D638/ISO 527 | 120 % | |
| Flexural modulus | ASTM D790 | 2500 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 58 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 83 MPa | |
| tensile strength | ISO 527-2 | 58.0 Mpa | |
| elongation | 断裂 | ASTM D638 | >150 % |
| Flexural modulus | ISO 178 | 2.4 Gpa | |
| bending strength | ISO 178 | 83.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 120 % |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 5.1 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 屈服 | ASTM D638 | 54.0 Mpa |
| ISO 527-1/-2 | 58 MPa |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/1200M |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.315 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 224 g/10min |
| physical property | Test Condition | Test Method | TORAY JAPAN/1200M |
|---|---|---|---|
| Viscosity value | 0.5%OCP | 内部方法 | 1.23 cm³/g |
| melt mass-flow rate | 250°C/1.0kg | ISO 1133 | 8.7 g/10min |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 16.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/1200M |
|---|---|---|---|
| melting temperature | 224 °C | ||
| UL flame retardant rating | UL94 | HB |