Impact strength of simply supported beam without notch
-30℃-30°C
ISO 179/1eU
-- kJ/m²
Impact strength of simply supported beam without notch
23℃23°C
ISO 179/1eU
-- kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shore hardness
Shore D,15 SecShore D,15 Sec
ISO 868
--
Shore hardness
球压硬度Ball Indentation Hardness
ISO 2039-1
-- Mpa
Shore hardness
拉伸模量Tensile Modulus
ISO 527-2
6500 Mpa
tensile strength
BreakBreak
ISO 527-2
120 Mpa
Tensile strain
BreakBreak
ISO 527-2
6 %
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8 MPa,Unannealed264 psi, Unannealed
ISO 75-2/A
165 °C
Hot deformation temperature
8.0 MPa,Unannealed1160 psi, Unannealed
ISO 75-2/C
90 °C
Continuous use temperature
---- 22
ISO 2578
90.0 to 120 °C
Continuous use temperature
---- 33
Internal Method
150 °C
Melting temperature
ISO 11357-3
180 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1.22 g/cm³
Water absorption rate
Saturation,23℃Saturation, 73°F
ISO 62
1.4 %
Water absorption rate
Equilibrium,23℃,50% RHEquilibrium, 73°F, 50% RH
ISO 62
0.6 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface resistivity
IEC 60093
-- ohms
Volume resistivity
IEC 60093
-- ohms·cm
Dielectric strength
IEC 60243-1
-- KV/mm
Compared to the anti leakage trace index
IEC 60112
V