PA12 LV-3A H EMS-CHEMIE SWITZERLAND
Grilamid®
Electrical applications、chip、Shell
Low temperature impact re、gas barrier
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/LV-3A H |
|---|---|---|---|
| Charpy Notched Impact Strength | 23℃23°C | ISO 179/1eA | -- kJ/m² |
| -30℃-30°C | ISO 179/1eA | -- kJ/m² | |
| Impact strength of simply supported beam without notch | -30℃-30°C | ISO 179/1eU | -- kJ/m² |
| 23℃23°C | ISO 179/1eU | -- kJ/m² |
| Electrical performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/LV-3A H |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | -- KV/mm | |
| Volume resistivity | IEC 60093 | -- ohms·cm | |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/LV-3A H |
|---|---|---|---|
| Shore hardness | 邵氏 D，15 秒邵氏 D，15 秒 | ISO 868 | -- |
| tensile strength | 断裂断裂 | ISO 527-2 | 120 Mpa |
| Shore hardness | 拉伸模量Tensile Modulus | ISO 527-2 | 6500 Mpa |
| Tensile strain | 断裂断裂 | ISO 527-2 | 6 % |
| Shore hardness | 球压硬度Ball Indentation Hardness | ISO 2039-1 | -- Mpa |
| physical property | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/LV-3A H |
|---|---|---|---|
| Water absorption rate | 平衡，23℃，50% RHEquilibrium, 73°F, 50% RH | ISO 62 | 0.6 % |
| 饱和，23℃Saturation, 73°F | ISO 62 | 1.4 % | |
| density | ISO 1183 | 1.22 g/cm³ |
| Thermal performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/LV-3A H |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 180 °C | |
| Heat distortion temperature | 1.8 MPa，未退火264 psi, Unannealed，HDT | ISO 75-2/A | 165 °C |
| 8.0 MPa，未退火1160 psi, Unannealed，HDT | ISO 75-2/C | 90 °C | |
| Continuous use temperature | ---- 33 | 内部方法 | 150 °C |
| ---- 22 | ISO 2578 | 90.0 to 120 °C |