Impact strength of simply supported beam without notch
23°C
ISO 179/1eA
9.0 kJ/m²
Charpy Notched Impact Strength
ASTM D256/ISO 179
7.5 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength
ASTM D256/ISO 179
25 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap
ASTM D256/ISO 179
60 kg·cm/cm(J/M)ft·lb/in
Elongation at Break
ASTM D412/ISO 527
2 %
Tensile modulus
ASTM D412/ISO 527
11500 kg/cm²(MPa)[Lb/in²]
tensile strength
ASTM D638/ISO 527
165 kg/cm²(MPa)[Lb/in²]
Rockwell hardness
ASTM D785
114
Bending modulus
ASTM D790/ISO 178
11500 kg/cm²(MPa)[Lb/in²]
bending strength
ASTM D790/ISO 178
250 kg/cm²(MPa)[Lb/in²]
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8 MPa,Unannealed
ISO 75-2/A
225 °C
Melting temperature
ISO 11357-3
255 °C
Linear coefficient of thermal expansion
Flow
ISO 11359-2
0.000030 cm/cm/°C
Linear coefficient of thermal expansion
Transverse
ISO 11359-2
0.000070 cm/cm/°C
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface resistivity
IEC 60093
ohms
Volume resistivity
IEC 60093
ohm·cm
Volume resistivity
IEC 60093
ohm·m