Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
65 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
70 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
Extreme Oxygen Index
ISO 4589-2
20 %
UL flame retardant rating
1.6mm
UL 94
HB
UL flame retardant rating
0.8mm
UL 94
HB
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
bending strength
23°C
ISO 178
240 Mpa
tensile strength
Break
ISO 527-2/1A/5
165 Mpa
Tensile strain
Break
ISO 527-2/1A/5
2.0 %
Tensile creep modulus
1hr
ISO 899-1
12500 Mpa
Tensile modulus
ISO 527-2/1A/1
17000 Mpa
Tensile creep modulus
1000hr
ISO 899-1
9500 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
8.0MPa,Unannealed
ISO 75-2/C
185 °C
Melting temperature
ISO 11357-3
225 °C
Vicat softening temperature
ISO 306/B50
225 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
215 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
1.5E-05 cm/cm/°C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
228 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
0.15 %
Melt Volume Flow Rate (MVR)
250°C/2.16kg
ISO 1133
5.00 cm3/10min
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Relative permittivity
100Hz
IEC 60250
4.40
Dissipation factor
1MHz
IEC 60250
0.019
Surface resistivity
IEC 60093
>1.0E+15 ohms
Relative permittivity
1MHz
IEC 60250
4.10
Volume resistivity
IEC 60093
>1.0E+15 ohms·cm
Dielectric strength
IEC 60243-1
35 KV/mm
Dissipation factor
100Hz
IEC 60250
1.6E-03