Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 2300GV1/50 CELANESE USA
CELANEX®
Electronic and electrical accessories,Automotive sector
High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/2300GV1/50 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| -30°C | ISO 179/1eU | 65 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/2300GV1/50 |
|---|---|---|---|
| Tensile creep modulus | 1hr | ISO 899-1 | 12500 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 17000 Mpa | |
| bending strength | 23°C | ISO 178 | 240 Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 9500 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 165 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.0 % |
| Electrical performance | Test Condition | Test Method | CELANESE USA/2300GV1/50 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.40 |
| Dissipation Factor | 100Hz | IEC 60250 | 1.6E-03 |
| relative permittivity | 1MHz | IEC 60250 | 4.10 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.019 |
| flammability | Test Condition | Test Method | CELANESE USA/2300GV1/50 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | CELANESE USA/2300GV1/50 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 5.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/2300GV1/50 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 228 °C |
| vicat | ISO 306/B50 | 225 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 215 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.5E-05 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 185 °C |