برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 3mmt,直径100mm 0.4 % Water absorption rate 23°C,60%RH ASTM D-570 0.28 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap Notch 3.2mmt ASTM D-256 8.0 Kgf.cm/cm bending strength 23°C ASTM D-790 2.500 Kgf/cm tensile strength 23°C ASTM D-638 1.700 Kgf/cm elongation 23°C ASTM D-638 3 % Bending modulus 23°C ASTM D-790 13.5 Rockwell hardness M scale ASTM D-785 M98 Impact strength of cantilever beam gap 3.2mmt Stype ASTM D-1822 160 Kgf.cm/cm Elongation at Break 2mmt ASTM D-732 820 Kgf/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D-1238 6 g/10 min Linear coefficient of thermal expansion 20°C -80°C ASTM D-696 1.5 Melting temperature 10°C/min DSC Method 165 °C Combustibility 0.8mmt UL -94 HB Hot deformation temperature 18.6kgf/cm ASTM D-648 163 °C Hot deformation temperature 4.6kgf/cm ASTM D-648 164 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون filler content 20 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D-257 2×10 Ω.cm Surface resistivity ASTM D-257 5×10 Ω
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.