برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون purpose 口罩
Other performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D-1238 500 g/10min Accelerated aging time ASTM D-3012 360 hr
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D-1238 3.0 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256/ISO 179 5 kg·cm/cm(J/M)ft·lb/in Elongation at Break ASTM D638/ISO 527 >500 % Shore hardness ASTM D-785 97 R scale Bending modulus ASTM D-790 15000 kg/cm Impact strength of cantilever beam gap 23℃ ASTM D-256 5 kg.cm/cm tensile strength Break ASTM D-638 370 kg/cm elongation Break ASTM D-638 >500 % Bending modulus ASTM D790/ISO 178 15000 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 97 tensile strength ASTM D638/ISO 527 370 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D-648 110 °C Vicat softening temperature ASTM D-1525 155 °C Vicat softening temperature ASTM D1525/ISO R306 155 ℃(℉) Hot deformation temperature HDT ASTM D648/ISO 75 110 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238/ISO 1133 500 g/10min