PP H230W SK KOREA
YUPLENE®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Other performance | Test Condition | Test Method | SK KOREA/H230W |
---|---|---|---|
Accelerated aging time | ASTM D-3012 | 360 hr | |
melt mass-flow rate | ASTM D-1238 | 500 g/10min |
Basic performance | Test Condition | Test Method | SK KOREA/H230W |
---|---|---|---|
melt mass-flow rate | ASTM D-1238 | 3.0 g/10min |
Mechanical properties | Test Condition | Test Method | SK KOREA/H230W |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 5 kg·cm/cm(J/M)ft·lb/in | |
23℃ | ASTM D-256 | 5 kg.cm/cm | |
elongation | 断裂 | ASTM D-638 | >500 % |
Flexural modulus | ASTM D790/ISO 178 | 15000 kg/cm²(MPa)[Lb/in²] | |
Shore hardness | ASTM D-785 | 97 R scale | |
Flexural modulus | ASTM D-790 | 15000 kg/cm | |
elongation at break | ASTM D638/ISO 527 | >500 % | |
Rockwell hardness | ASTM D785 | 97 | |
tensile strength | ASTM D638/ISO 527 | 370 kg/cm²(MPa)[Lb/in²] | |
断裂 | ASTM D-638 | 370 kg/cm |
other | Test Condition | Test Method | SK KOREA/H230W |
---|---|---|---|
purpose | 口罩 |
Physical properties | Test Condition | Test Method | SK KOREA/H230W |
---|---|---|---|
melt mass-flow rate | ASTM D1238/ISO 1133 | 500 g/10min |
Thermal performance | Test Condition | Test Method | SK KOREA/H230W |
---|---|---|---|
Heat distortion temperature | HDT | ASTM D-648 | 110 °C |
HDT | ASTM D648/ISO 75 | 110 ℃(℉) | |
vicat | ASTM D1525/ISO R306 | 155 ℃(℉) | |
ASTM D-1525 | 155 °C |