برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C,3.18mm ASTM D256 200 J/m Impact strength of cantilever beam gap 23°C,6.35mm ASTM D256 180 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.6mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield,23°C,3.18mm ASTM D638 42.1 Mpa tensile strength Break,23°C,3.18mm ASTM D638 35.2 Mpa elongation Break,23°C,3.18mm ASTM D638 30 % Bending modulus 23°C ASTM D790 2550 Mpa bending strength Yield,23°C ASTM D790 73.5 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed,12.7mm ASTM D648 83.0 °C Vicat softening temperature ASTM D15254 103 °C RTI Elec 1.6mm UL 746 60.0 °C RTI Imp 1.6mm UL 746 60.0 °C RTI Str 1.6mm UL 746 60.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.04 g/cm³ melt mass-flow rate 200°C/5.0kg ASTM D1238 2.0 g/10min melt mass-flow rate 220°C/10.0kg ASTM D1238 20 g/10min Shrinkage rate MD ASTM D955 <0.40 % Water absorption rate 24hr ASTM D570 <0.30 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون High arc combustion index 1.57mm UL 746 PLC 0 High voltage arc tracing rate 1.57mm UL 746 mm/min Hot wire ignition 1.57mm UL 746 PLC 3 sec
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Sale,23°C ASTM D785 115