Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 5000 TAIDA TAIWAN
TAITALAC®
Household goods、Audiotape、Shell、Electrical appliances
High rigidity
UL
TDS
TDS_ISO
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIDA TAIWAN/5000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 180 J/m |
| 23°C,3.18mm | ASTMD256 | 200 J/m |
| hardness | Test Condition | Test Method | TAIDA TAIWAN/5000 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTMD785 | 115 |
| Electrical performance | Test Condition | Test Method | TAIDA TAIWAN/5000 |
|---|---|---|---|
| High arc combustion index (HAI) | 1.57mm | UL746 | 200 |
| High voltage arc ignition resistance index | 1.57mm | UL746 | 0.00 mm/min |
| Hot-wireIgnition | 1.57mm | UL746 | 18 sec |
| Mechanical properties | Test Condition | Test Method | TAIDA TAIWAN/5000 |
|---|---|---|---|
| Tensile strength 2 | Break,23°C,3.18mm | ASTMD638 | 35.2 Mpa |
| tensile strength | 屈服,23°C,3.18mm | ASTMD638 | 42.1 Mpa |
| elongation | 断裂,23°C,3.18mm | ASTMD638 | 30 % |
| Flexural modulus | 23°C | ASTMD790 | 2550 Mpa |
| bending strength | 屈服,23°C | ASTMD790 | 73.5 Mpa |
| flammability | Test Condition | Test Method | TAIDA TAIWAN/5000 |
|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | TAIDA TAIWAN/5000 |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTMD1238 | 2.0 g/10min |
| density | ASTMD792 | 1.04 g/cm³ | |
| Shrinkage rate | MD | ASTMD955 | <0.40 % |
| Water absorption rate | 24hr | ASTMD570 | <0.30 % |
| melt mass-flow rate | 220°C/10.0kg | ASTMD1238 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | TAIDA TAIWAN/5000 |
|---|---|---|---|
| RTI Elec | 1.6mm | UL746 | 60.0 °C |
| 1.8MPa,未退火,12.7mm | ASTMD648 | 83.0 °C | |
| RTI Str | 1.6mm | UL746 | 60.0 °C |
| RTI Imp | 1.6mm | UL746 | 60.0 °C |
| vicat | ASTMD15254 | 103 °C |