physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	190°C/2.16 kg	ISO 1133	22 g/10 min
melt mass-flow rate	melt mass-flow rate	210°C/2.16 kg	ISO 1133	50 g/10 min
water content		Karl Fisher	< 400 ppm

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2	3500 Mpa
tensile strength		ISO 527-2	50.0 Mpa
Tensile strain	断裂	ISO 527-2	< 5.0 %

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			100 °C
drying time			4.0 to 6.0 hr
Dew point temperature			< -40 °C
Suggested maximum moisture content			0.025 %
Hopper temperature			20 to 40 °C
Temperature at the rear of the barrel			155 to 175 °C
Temperature in the middle of the barrel			180 to 220 °C
Spray nozzle temperature			180 to 220 °C
Processing (melt) temperature			180 to 220 °C
Back pressure			5.00 to 10.0 Mpa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45 MPa, 未退火3，HDT	ISO 75-2/Bf	55.0 to 60.0 °C
Heat distortion temperature	Heat distortion temperature	0.45 MPa, 未退火4，HDT	ISO 75-2/Bf	100 to 110 °C
Glass Transition Temperature		DSC	55.0 to 60.0 °C
melting temperature		DSC	175 °C
Monomer Residue		内部方法	< 0.30 %