برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D-1238 10.5 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ASTM D-790 2343 Mpa tensile strength 屈伏点 ASTM D-638 62 Mpa Elongation at Break Break点 ASTM D-638 130 % Impact strength of cantilever beam gap Notched23°C ASTM D-256 800 J/m bending strength ASTM D-790 96 Mpa tensile strength Break点 ASTM D-638 69 Mpa Rockwell hardness R ASTM D-785 118
thermal performance شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 1.1 mm Linear coefficient of thermal expansion E831 6.8×10 1/°C Hot deformation temperature 0.45MPa ASTM D-648 137 °C Long term use temperature UL 746B 130 °C Vicat softening temperature ASTM D-1525 154 °C UL flame retardant rating UL94 HB Hot deformation temperature 1.8MPa ASTM D-648 132 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 3.2mm ASTM D-955 5-7 10 density ASTM D-792 1.2 Water absorption rate % ASTM D-570 0.15
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dissipation factor 60Hz ASTM D-150 0.0009 Dielectric constant 60Hz ASTM D-150 3.17 Dissipation factor 1MHz ASTM D-150 0.01 Dielectric constant 1MHz ASTM D-150 2.96 Volume resistivity ASTM D-257 1.0×10 ohm-cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.