برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,3.20mm,Injection,总能量 ASTM D3763 58.8 J
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.50mm UL 94 V-0 UL flame retardant rating 3.00mm UL 94 V-0 Burning wire flammability index 1.00mm IEC 60695-2-12 960 °C Extreme Oxygen Index ASTM D2863 35 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation Break,3.20mm,Injection ASTM D638 110 % Bending modulus 3.20mm,Injection ASTM D790 2400 Mpa bending strength 3.20mm,Injection ASTM D790 93.8 Mpa Tensile modulus 3.20mm,Injection ASTM D638 2210 Mpa tensile strength Yield,3.20mm,Injection ASTM D638 60.0 Mpa tensile strength Break,3.20mm,Injection ASTM D638 57.9 Mpa elongation Yield,3.20mm,Injection ASTM D638 6.2 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed ASTM D648 139 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 127 °C Vicat softening temperature ASTM D15252 149 °C Linear coefficient of thermal expansion MD:-40to82°C ASTM D696 6.5E-05 cm/cm/°C RTI Elec 3.20mm UL 746 125 °C RTI Imp 3.20mm UL 746 125 °C RTI 3.20mm UL 746 125 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 300°C/1.2kg ASTM D1238 7.0 g/10min Shrinkage rate MD ASTM D955 0.50-0.70 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale,3.20mm,Injection ASTM D785 123