PC 8600 WH STYRON TAIWAN
EMERGE™
--
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | STYRON TAIWAN/8600 WH |
|---|---|---|---|
| Dart impact equipped with measuring instruments 1 | 23°C,3.20mm,注塑,总能量 | ASTMD3763 | 58.8 J |
| hardness | Test Condition | Test Method | STYRON TAIWAN/8600 WH |
|---|---|---|---|
| Rockwell hardness | R级,3.20mm,注塑 | ASTMD785 | 123 |
| Mechanical properties | Test Condition | Test Method | STYRON TAIWAN/8600 WH |
|---|---|---|---|
| bending strength | 3.20mm,注塑 | ASTMD790 | 93.8 Mpa |
| Tensile modulus | 3.20mm,注塑 | ASTMD638 | 2210 Mpa |
| tensile strength | 断裂,3.20mm,注塑 | ASTMD638 | 57.9 Mpa |
| elongation | 屈服,3.20mm,注塑 | ASTMD638 | 6.2 % |
| 断裂,3.20mm,注塑 | ASTMD638 | 110 % | |
| Flexural modulus | 3.20mm,注塑 | ASTMD790 | 2400 Mpa |
| tensile strength | 屈服,3.20mm,注塑 | ASTMD638 | 60.0 Mpa |
| flammability | Test Condition | Test Method | STYRON TAIWAN/8600 WH |
|---|---|---|---|
| Extreme Oxygen Index 5 | ASTMD2863 | 35 % | |
| UL flame retardant rating 3 | 1.50mm | UL94 | V-0 |
| 3.00mm | UL94 | V-0 | |
| Burning wire flammability index 4 | 1.00mm | IEC60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | STYRON TAIWAN/8600 WH |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 7.0 g/10min |
| Shrinkage rate | MD | ASTMD955 | 0.50到0.70 % |
| Thermal performance | Test Condition | Test Method | STYRON TAIWAN/8600 WH |
|---|---|---|---|
| 0.45MPa,未退火 | ASTMD648 | 139 °C | |
| RTI Imp | 3.20mm | UL746 | 125 °C |
| MD：-40到82°C | ASTMD696 | 6.5E-05 cm/cm/°C | |
| RTI | 3.20mm | UL746 | 125 °C |
| RTI Elec | 3.20mm | UL746 | 125 °C |
| 1.8MPa,未退火 | ASTMD648 | 127 °C | |
| vicat | ASTMD15252 | 149 °C |