| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.26 g/cm³ |
| melt mass-flow rate | 240°C/2.16kg | ISO 1133 | 13 g/10min |
| Melt volume flow rate | 240°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.6 % |
| Shrinkage rate | MD | ISO 294-4 | 1.6 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.60 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏D | ISO 868 | 68 |
| Shore hardness | 邵氏D,15秒 | ISO 868 | 64 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Limiting Oxygen Index | | ISO 4589-2 | 23 % |
| burning rate | 1.00mm | ISO 3795 | DNI |
| UL flame retardant rating | 1.5mm | UL 94,IEC60695-11-10,-20 | HB |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Emissions of Organic Compounds | | VDA277 | 300 µgC/g |
| Filling analysis | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt density | | | 1.11 g/cm³ |
| SpecificHeatCapacity of Melt | | | 2150 J/kg/°C |
| ThermalConductivityofMelt | | | 0.15 W/m/K |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 8256/1 | 300 kJ/m² |
| Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 36 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 38 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile creep modulus | 1000hr | ISO 899-1 | 310 Mpa |
| Flexural modulus | | ISO 178 | 550 Mpa |
| wear resistance | | ISO 4649 | 100 mm³ |
| Tensile modulus | | ISO 527-2 | 550 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 26.0 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 50.0 Mpa |
| tensile strength | 5.0%应变 | ISO 527-2 | 14.0 Mpa |
| tensile strength | 10%应变 | ISO 527-2 | 23.0 Mpa |
| tensile strength | 50%应变 | ISO 527-2 | 24.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 26 % |
| Tensile strain | 断裂 | ISO 527-2 | >300 % |
| Nominal tensile fracture strain | | ISO 527-2 | 530 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 360 Mpa |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tear strength | 横向流量 | ISO 34-1 | 170 kN/m |
| tear strength | 流量 | ISO 34-1 | 180 kN/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 2E+12 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20 KV/mm |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.016 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.030 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | EffectiveThermalDiffusivity | ISO 11359-2 | 8E-08 m²/s |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 100 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 50.0 °C |
| brittle temperature | | ISO 974 | -97.0 °C |
| Glass Transition Temperature | | ISO 11357-2 | 25.0 °C |
| vicat | -- | ISO 306/A50 | 205 °C |
| vicat | -- | ISO 306/B50 | 140 °C |
| melting temperature | | ISO 11357-3 | 218 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.7E-04 cm/cm/°C |