Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPEE 7246 DUPONT TAIWAN
BEXLOY®
Medical supplies、Nursing supplies、film、Casters、Other sheets、building materials、Profile
Thermal stability、Aging resistance、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 36 kJ/m² |
| Tensile impact strength | 23°C | ISO8256/1 | 300 kJ/m² |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 38 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 7.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 300 µgC/g |
| hardness | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| 邵氏D,15秒 | ISO868 | 64 | |
| 邵氏D | ISO868 | 68 |
| Electrical performance | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC60250 | 0.030 |
| CTI | IEC60112 | 600 V | |
| 1MHz | IEC60250 | 3.50 | |
| Volume resistivity | IEC60093 | 2E+12 ohms·cm | |
| dielectric strength | IEC60243-1 | 20 KV/mm | |
| 100Hz | IEC60250 | 4.00 | |
| Dissipation Factor | 100Hz | IEC60250 | 0.016 |
| Mechanical properties | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2 | 26.0 Mpa |
| 50%应变 | ISO527-2 | 24.0 Mpa | |
| Tensile modulus | ISO527-2 | 550 Mpa | |
| Tensile creep modulus | 1000hr | ISO899-1 | 310 Mpa |
| Tensile stress | 5.0%应变 | ISO527-2 | 14.0 Mpa |
| Tensile strain | 断裂 | ISO527-2 | >300 % |
| Nominal tensile fracture strain | ISO527-2 | 530 % | |
| Tensile stress | 断裂 | ISO527-2 | 50.0 Mpa |
| 10%应变 | ISO527-2 | 23.0 Mpa | |
| Tensile creep modulus | 1hr | ISO899-1 | 360 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 26 % |
| Flexural modulus | ISO178 | 550 Mpa | |
| abrasion resistance | ISO4649 | 100 mm³ |
| flammability | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| Burning rate 4 | 1.00mm | ISO3795 | DNI |
| UL flame retardant rating | 1.5mm | UL94,IEC60695-11-10,-20 | HB |
| Limiting Oxygen Index | ISO4589-2 | 23 % |
| Filling analysis | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| ThermalConductivityofMelt | 0.15 W/m/K | ||
| SpecificHeatCapacity of Melt | 2150 J/kg/°C | ||
| Melt density | 1.11 g/cm³ |
| physical property | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.6 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 0.60 % |
| Melt volume flow rate | 240°C/2.16kg | ISO1133 | 12.0 cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 1.6 % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.30 % |
| density | ISO1183 | 1.26 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % |
| melt mass-flow rate | 240°C/2.16kg | ISO1133 | 13 g/10min |
| elastomer | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| tear strength | 横向流量 | ISO34-1 | 170 kN/m |
| 流量 | ISO34-1 | 180 kN/m |
| Thermal performance | Test Condition | Test Method | DUPONT TAIWAN/7246 |
|---|---|---|---|
| TD | ISO11359-2 | 1.7E-04 cm/cm/°C | |
| EffectiveThermalDiffusivity | ISO11359-2 | 8E-08 m²/s | |
| 0.45MPa,未退火 | ISO75-2/B | 100 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 50.0 °C | |
| vicat | -- | ISO306/A50 | 205 °C |
| Melting temperature 3 | ISO11357-3 | 218 °C | |
| MD | ISO11359-2 | 1.8E-04 cm/cm/°C | |
| brittle temperature | ISO974 | -97.0 °C | |
| Glass transition temperature 3 | ISO11357-2 | 25.0 °C | |
| vicat | -- | ISO306/B50 | 140 °C |