Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
85 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
85 kJ/m²
Impact strength of cantilever beam gap
-40°C
ISO 180/1A
5.0 kJ/m²
Impact strength of cantilever beam gap
23°C
ISO 180/1A
8.0 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
Flammability level
UL 94
V-0
Flammability level
UL 94
V-0
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2
3000 Mpa
tensile strength
Yield
ISO 527-2
60.0 Mpa
Nominal tensile fracture strain
ISO 527-2
20 %
Bending modulus
ISO 178
2500 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8 MPa, Unannealed
ISO 75-2/A
160 °C
Melting temperature
ISO 11357-3
295 °C
Linear coefficient of thermal expansion
Flow
ISO 11359-2
9.0E-5 cm/cm/°C
Linear coefficient of thermal expansion
Across Flow
ISO 11359-2
9.0E-5 cm/cm/°C
RTI Elec
0.75 mm
UL 746
65.0 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1.37 g/cm³
Shrinkage rate
横向Flow
ISO 294-4
2.0 %
Shrinkage rate
Flow
ISO 294-4
2.0 %
Water absorption rate
Equilibrium, 23°C, 50% RH
ISO 62
2.0 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.