برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Multi axis Instrumented Impact Energy ISO 6603-2 1.00 J Dart impact 23°C,EnergyatPeakLoad ASTM D3763 3.00 J Suspended wall beam without notch impact strength 23°C ISO 180/1U 91 kJ/m² Impact strength of cantilever beam gap 23°C ISO 180/1A 8.8 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Wear factor Washer ASTM D3702Modified 128 10^-10in^5-min/ft-lb-hr Friction coefficient Static ASTM D3702Modified 0.43 Friction coefficient Dynamic ASTM D3702Modified 0.52 bending strength ISO 178 118 Mpa bending strength ASTM D790 117 Mpa Bending modulus ISO 178 3320 Mpa Bending modulus ASTM D790 2960 Mpa Tensile strain Break ISO 527-2 12 % elongation Break ASTM D638 23 % Tensile strain Yield ISO 527-2 5.0 % elongation Yield ASTM D638 5.8 % tensile strength Break ISO 527-2 69.0 Mpa tensile strength Break ASTM D638 69.6 Mpa tensile strength Yield ISO 527-2 73.0 Mpa tensile strength Yield ASTM D638 74.5 Mpa Tensile modulus ISO 527-2/1 3070 Mpa Tensile modulus ASTM D638 2900 Mpa
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:24hr ISO 294-4 1.3 % Shrinkage rate TD:24hr ISO 294-4 1.9 % Shrinkage rate TD:24hr ASTM D955 1.9 % Shrinkage rate MD:24hr ASTM D955 1.3 % Water absorption rate 24hr,50%RH ASTM D570 0.060 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.