Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK LL004C SABIC INNOVATIVE US
LNP™ LUBRICOMP™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/LL004C |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 91 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 1.00 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.8 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 3.00 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/LL004C |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3070 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.8 % |
| bending strength | ASTM D790 | 117 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| tensile strength | 断裂 | ASTM D638 | 69.6 Mpa |
| 断裂 | ISO 527-2 | 69.0 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 128 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | ASTM D790 | 2960 Mpa | |
| Tensile modulus | ASTM D638 | 2900 Mpa | |
| elongation | 断裂 | ASTM D638 | 23 % |
| bending strength | ISO 178 | 118 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.43 |
| Tensile strain | 断裂 | ISO 527-2 | 12 % |
| Flexural modulus | ISO 178 | 3320 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 74.5 Mpa |
| 屈服 | ISO 527-2 | 73.0 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.52 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/LL004C |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 1.3 % |
| MD：24小时 | ASTM D955 | 1.3 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.060 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 1.9 % |
| TD:24小时 | ISO 294-4 | 1.9 % |