Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
35 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
25 kJ/m²
Impact strength of cantilever beam gap
23°C
ISO 180/1A
6.0 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2/1A/1
8600 Mpa
tensile strength
Break,-40°C
ASTM D638
159 Mpa
tensile strength
Break,23°C
ASTM D638
110 Mpa
tensile strength
Break,71°C
ASTM D638
68.9 Mpa
tensile strength
Break
ISO 527-2/1A/5
106 Mpa
Tensile strain
Break
ISO 527-2/1A/5
2.0 %
Bending modulus
23°C
ISO 178
8700 Mpa
bending strength
23°C
ISO 178
160 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8MPa,Unannealed
ASTM D648
163 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
160 °C
Melting temperature
ASTM D3418
166 °C
Melting temperature
ISO 11357-3
165 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
2.5E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD
ISO 11359-2
1.2E-04 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ASTM D792
1.58 g/cm³
density
ISO 1183
1.58 g/cm³
Shrinkage rate
MD
ASTM D955
0.40 %
Shrinkage rate
TD
ASTM D955
1.4 %
Shrinkage rate
TD
ISO 294-4
1.2 %
Shrinkage rate
MD
ISO 294-4
0.40 %
Water absorption rate
Saturation,23°C
ISO 62
0.80 %
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
0.20 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
ASTM D257
1.4E+14 ohms·cm