برگه داده فنی مقایسهOther performance شرایط آزمون روش آزمون نتیجه آزمون Extreme Oxygen Index 干 ASTM D2863 26 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 湿 ASTM D256 147 J/m Rockwell hardness 干 ASTM D785 80 M Rockwell hardness 湿 ASTM D785 55 M Rockwell hardness 干 ASTM D785 120 R Rockwell hardness 湿 ASTM D785 108 R tensile strength 干 ASTM D638 79 Mpa tensile strength 湿 ASTM D638 57 Mpa Elongation at Break 干 ASTM D638 50 % Elongation at Break 湿 ASTM D638 250 % bending strength 干 ASTM D790 118 Mpa bending strength 湿 ASTM D790 54 Mpa Bending modulus 干 ASTM D790 2.8 GPa Bending modulus 湿 ASTM D790 1.2 GPa Impact strength of cantilever beam gap 干 ASTM D256 39 J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion 干 ASTM D696 8 Hot deformation temperature 1.82MPa ASTM D648 70 °C Hot deformation temperature 0.46MPa ASTM D648 230 °C thermal conductivity 干 0.2 W/(m.K) UL flame retardant rating 干 UL 94 V-2
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 湿 2.5 % Shrinkage rate 干 1.3-2.0 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.