Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1402 ASAHI JAPAN
Leona™
Washer、Hose、Wire sheath
Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | ASAHI JAPAN/1402 |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D2863 | 26 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1402 |
|---|---|---|---|
| Rockwell hardness | 干 | ASTM D785 | 80 M |
| bending strength | 干 | ASTM D790 | 118 Mpa |
| elongation at break | 干 | ASTM D638 | 50 % |
| Flexural modulus | 湿 | ASTM D790 | 1.2 GPa |
| Rockwell hardness | 干 | ASTM D785 | 120 R |
| Impact strength of cantilever beam gap | 湿 | ASTM D256 | 147 J/m |
| tensile strength | 干 | ASTM D638 | 79 Mpa |
| 湿 | ASTM D638 | 57 Mpa | |
| elongation at break | 湿 | ASTM D638 | 250 % |
| Impact strength of cantilever beam gap | 干 | ASTM D256 | 39 J/m |
| Rockwell hardness | 湿 | ASTM D785 | 55 M |
| bending strength | 湿 | ASTM D790 | 54 Mpa |
| Flexural modulus | 干 | ASTM D790 | 2.8 GPa |
| Rockwell hardness | 湿 | ASTM D785 | 108 R |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1402 |
|---|---|---|---|
| Shrinkage rate | 干 | 1.3-2.0 % | |
| Water absorption rate | 湿 | 2.5 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1402 |
|---|---|---|---|
| Heat distortion temperature | 0.46MPa，HDT | ASTM D648 | 230 °C |
| Linear coefficient of thermal expansion | 干 | ASTM D696 | 8 |
| thermal conductivity | 干 | 0.2 W/(m.K) | |
| UL flame retardant rating | 干 | UL 94 | V-2 |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D648 | 70 °C |