Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
35 kJ/m²
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
35 kJ/m²
tensile strength
23°C
ISO 527-2
110 Mpa
Elongation at Break
23°C
ISO 527-2
3.0 %
Tensile modulus
23°C
ISO 527-2
6100 Mpa
Tensile creep modulus
1Hr
ISO 899-1
5300 Mpa
Tensile creep modulus
1000Hr
ISO 899-1
4300 Mpa
bending strength
23°C
ISO 178
160 Mpa
Charpy Notched Impact Strength
23°C
ISO 179/1eA
6.5 kJ/m²
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPaUnannealed
ISO 75-2/Bf
190 °C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
65.0 °C
Vicat softening temperature
ISO 306/B50
210 °C
Vicat softening temperature
Melting Temperature
ISO 11357-3
255 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
3.5E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Water absorption rate
(23°C,50RH)
ISO 62
0.15 %
melt mass-flow rate
℃/Kg
ISO 1133
21.0 cm3/10min
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
1E+11 Ω.cm
Surface resistivity
IEC 60093
>1.0E+15 Ω.cm
Dielectric strength
IEC 60243-1
32 KV/mm
Dielectric constant
23°C
IEC 60250
4.00 1MHz
Dissipation factor
23°C
IEC 60250
0.02 1MHz
Dissipation factor
相对漏电起痕指数
IEC 60112
250 V
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL -94
HB 0.85mm
UL flame retardant rating
UL -94
HB 1.20mm
UL flame retardant rating
UL -94
HB 1.40mm
UL flame retardant rating
UL -94
HB 3.00mm
Extreme Oxygen Index
ISO 4589-2
19 %