PBT 2302 GV1/15 CELANESE USA
CELANEX®
Electronic and electrical accessories,Automotive sector
High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/2302 GV1/15 |
|---|---|---|---|
| Tensile creep modulus | 1Hr | ISO 899-1 | 5300 Mpa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.5 kJ/m² |
| bending strength | 23°C | ISO 178 | 160 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.5 kJ/m² |
| Tensile creep modulus | 1000Hr | ISO 899-1 | 4300 Mpa |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 35 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2 | 6100 Mpa |
| elongation at break | 23°C | ISO 527-2 | 3.0 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/2302 GV1/15 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 250 V |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| dielectric constant | 23°C | IEC 60250 | 4.00 1MHz |
| Surface Resistivity | IEC 60093 | >1.0E+15 Ω.cm | |
| Dissipation Factor | 23°C | IEC 60250 | 0.02 1MHz |
| Volume resistivity | IEC 60093 | 1E+11 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | CELANESE USA/2302 GV1/15 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.40mm | |
| Limiting Oxygen Index | ISO 4589-2 | 19 % | |
| UL flame retardant rating | UL -94 | HB 1.20mm | |
| UL -94 | HB 3.00mm | ||
| UL -94 | HB 0.85mm |
| physical property | Test Condition | Test Method | CELANESE USA/2302 GV1/15 |
|---|---|---|---|
| melt mass-flow rate | ℃/Kg | ISO 1133 | 21.0 cm3/10min |
| Water absorption rate | (23°C,50RH) | ISO 62 | 0.15 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/2302 GV1/15 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 65.0 °C |
| vicat | ISO 306/B50 | 210 °C | |
| 熔融温度 | ISO 11357-3 | 255 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 190 °C |