برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون Transmittance rate 1.5mmt JIS K7136 59 % Pigment dispersion 2.0mmt In-house method 60 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength 50mm/min,Yield ISO 527-1 61 Mpa tensile strength 50mm/min,Break ISO 527-1 65 Mpa Elongation at Break 50mm/min ISO 527-1 120 % Bending modulus 2mm/min ISO 178 2200 Mpa bending strength 2mm/min ISO 178 95 Mpa Impact strength of cantilever beam gap Notched ISO 179 20 kJ/m² Impact strength of cantilever beam gap ASTM D256/ISO 179 20 kg·cm/cm(J/M)ft·lb/in Elongation at Break ASTM D638/ISO 527 66 % tensile strength ASTM D638/ISO 527 61 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 2300 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 96 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 120 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.80MPa ISO 75-1 129 °C Hot deformation temperature 阻燃性,1.0mm/3.0mm UL 94 V-2 Hot deformation temperature HDT ASTM D648/ISO 75 122 ℃(℉) Linear coefficient of thermal expansion ASTM D696/ISO 11359 0.7 mm/mm.℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Dissolving fingers 300℃ ISO 1133 8 cm310min Shrinkage rate ASTM D955 0.5-0.7 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.