برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus 23°C ASTM D638 9720 Mpa tensile strength 23°C ASTM D638 121 Mpa elongation Break, 23°C ASTM D638 2.0 % Bending modulus 23°C ASTM D790 11000 Mpa bending strength 23°C ASTM D790 172 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 121 °C drying time 2.0 to 4.0 hr Suggested maximum moisture content 0.10 % Temperature at the rear of the barrel 302 to 316 °C Temperature in the middle of the barrel 316 to 332 °C Temperature at the front of the material cylinder 310 to 327 °C Spray nozzle temperature 310 to 327 °C Processing (melt) temperature 304 to 327 °C Mold temperature 71 to 88 °C Injection speed 中等 Back pressure 0.00 to 0.689 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45 MPa, Unannealed ASTM D648 146 °C Hot deformation temperature 1.8 MPa, Unannealed ASTM D648 142 °C Linear coefficient of thermal expansion Flow ASTM D696 3.2E-5 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 3.18 mm,Flow ASTM D955 0.15 % Water absorption rate 24 hr ASTM D570 0.15 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D257 1.0E+2 - 5.5E+5 ohms Volume resistivity ASTM D257 1.0E+2 - 1.0E+5 ohms·cm