PC/CF CF15 LNP JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LNP JAPAN/CF15 |
|---|---|---|---|
| elongation | 断裂, 23°C | ASTM D638 | 2.0 % |
| bending strength | 23°C | ASTM D790 | 172 Mpa |
| Tensile modulus | 23°C | ASTM D638 | 9720 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 11000 Mpa |
| tensile strength | 23°C | ASTM D638 | 121 Mpa |
| Electrical performance | Test Condition | Test Method | LNP JAPAN/CF15 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+2 - 1.0E+5 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1.0E+2 - 5.5E+5 ohms |
| physical property | Test Condition | Test Method | LNP JAPAN/CF15 |
|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.15 % |
| Shrinkage rate | 3.18 mm，Flow | ASTM D955 | 0.15 % |
| Thermal performance | Test Condition | Test Method | LNP JAPAN/CF15 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ASTM D648 | 146 °C |
| 1.8 MPa, 未退火，HDT | ASTM D648 | 142 °C | |
| Linear coefficient of thermal expansion | 流动 | ASTM D696 | 3.2E-5 cm/cm/°C |
| injection | Test Condition | Test Method | LNP JAPAN/CF15 |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.10 % | ||
| Temperature in the middle of the barrel | 316 to 332 °C | ||
| Temperature at the rear of the barrel | 302 to 316 °C | ||
| Processing (melt) temperature | 304 to 327 °C | ||
| drying temperature | 121 °C | ||
| Temperature at the front of the material cylinder | 310 to 327 °C | ||
| Back pressure | 0.00 to 0.689 Mpa | ||
| Temperature | 71 to 88 °C | ||
| injection speed | 中等 | ||
| Spray nozzle temperature | 310 to 327 °C |