برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون density ASTM D-1505 0.925 melt mass-flow rate ASTM D-1238 2 g/10
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break ASTM D638/ISO 527 340 % Elongation at Break ASTM D638/ISO 527 27 % Elongation at Break ASTM D-6398 620 % Elongation at Break ASTM D-6398 340 % Impact strength of cantilever beam gap ASTM D-1709 A-B 大于等于140 g tear strength ASTM D-1922 167 g tear strength ASTM D-1922 239 g Shore hardness ASTM D-2240 40 Shore hardness ASTM D-2240 95 Secant modulus 1%Strain, Break ASTM D-882B 130 N/mm Secant modulus 1%Strain, Break ASTM D-882B 124 N/mm tensile strength Break ASTM D-638 19 N/mm tensile strength Break ASTM D-638 27 N/mm tensile strength Yield ASTM D-638 7.5 N/mm tensile strength Yield ASTM D-638 8.2 N/mm Shore hardness ASTM D2240/ISO 868 95 Shore A Shore hardness ASTM D2240/ISO 868 40 Shore D
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D-1525 90 °C Melting temperature 104 °C Melting temperature 104 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون film thickness 40 u turbidity ASTM D-2457 5 % Vinyl acetate content ISC.DIS 8965/1989(E) 5 % gloss ASTM D-1003A 70 % Vinyl acetate content 5 % density ASTM D1505 0.925 g/cm²
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric constant ASTM D150/IEC 60250 750 Dielectric constant ASTM D150/IEC 60250 2.6 Dielectric constant ASTM D-150 2.6 Dielectric strength ASTM D-149 750 KV/cm