برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C,6.40mm ASTM D256 88 J/m Impact strength of cantilever beam gap -30°C,3.20mm ASTM D256 59 J/m Impact strength of cantilever beam gap -30°C,6.40mm ASTM D256 49 J/m Impact strength of cantilever beam gap 23°C,3.20mm ASTM D256 130 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.6mm UL 94 HB UL flame retardant rating 3.2mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus 3.20mm ASTM D638 1780 Mpa tensile strength Yield,3.20mm ASTM D638 26.5 Mpa elongation Yield,3.20mm ASTM D638 5.0 % elongation Break,3.20mm ASTM D638 62 % Bending modulus 3.20mm ASTM D790 2130 Mpa bending strength 3.20mm ASTM D790 42.2 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed,6.40mm ASTM D648 91.0 °C Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 82.0 °C Vicat softening temperature ASTM D15255 90.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.03 g/cm³ melt mass-flow rate 200°C/5.0kg ASTM D1238 6.0 g/10min melt mass-flow rate 220°C/10.0kg ASTM D1238 65 g/10min melt mass-flow rate 230°C/3.8kg ASTM D1238 15 g/10min
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale ASTM D785 99
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.