HIPS 60HRI LG CHEM KOREA
--
Household appliances、Home appliance components
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/60HRI |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 88 J/m |
| 23°C,3.20mm | ASTM D256 | 130 J/m | |
| -30°C,6.40mm | ASTM D256 | 49 J/m | |
| -30°C,3.20mm | ASTM D256 | 59 J/m |
| hardness | Test Condition | Test Method | LG CHEM KOREA/60HRI |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 99 |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/60HRI |
|---|---|---|---|
| Tensile modulus | 3.20mm | ASTM D638 | 1780 Mpa |
| elongation | 断裂,3.20mm | ASTM D638 | 62 % |
| tensile strength | 屈服,3.20mm | ASTM D638 | 26.5 Mpa |
| elongation | 屈服,3.20mm | ASTM D638 | 5.0 % |
| Flexural modulus | 3.20mm | ASTM D790 | 2130 Mpa |
| bending strength | 3.20mm | ASTM D790 | 42.2 Mpa |
| flammability | Test Condition | Test Method | LG CHEM KOREA/60HRI |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LG CHEM KOREA/60HRI |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 6.0 g/10min |
| 230°C/3.8kg | ASTM D1238 | 15 g/10min | |
| density | ASTM D792 | 1.03 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 65 g/10min |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/60HRI |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 82.0 °C |
| vicat | ASTM D15255 | 90.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 91.0 °C |