برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength 23°C ASTM D638 86 Mpa Elongation at Break 23°C ASTM D638 1.5 % Tensile modulus 23°C ASTM D638 7650 Mpa bending strength 23°C ASTM D790 114 Mpa Bending modulus 23°C ASTM D790 6660 Mpa Impact strength of cantilever beam gap 23°C ASTM D256 48 J/m Suspended wall beam without notch impact strength 23°C ASTM D4812 230 J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPaUnannealed ASTM D648 105 °C Hot deformation temperature 1.80MPaUnannealed ASTM D648 101 °C Linear coefficient of thermal expansion MD ASTM D696 3.3E-05 cm/cm/°C Linear coefficient of thermal expansion TD ASTM D696 8.3E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD ASTM D995 0.2-0.4 % Shrinkage rate TD ASTM D995 0.3-0.5 % Water absorption rate (23°C,50RH) ASTM D570 0.23 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D257 3 Ω.cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.