Impact strength of simply supported beam without notch
23℃
ISO 179/1eU
46 KJ/m
Impact strength of simply supported beam without notch
-30℃
ISO 179/1eU
45 KJ/m
Charpy Notched Impact Strength
23℃
ISO 179/1eA
8.5 KJ/m
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Melting temperature
ISO 11357-1
225 °C
Glass transition temperature
ISO 11357-1
60 °C
Hot deformation temperature
1.8Mpa
ISO 75-1/-2
205 °C
Hot deformation temperature
0.45Mpa
ISO 75-1/-2
225 °C
Vicat softening temperature
ISO 306
220 °C
Linear coefficient of thermal expansion
Across Flow
ISO 11359-2
0.25 E-4/℃
Linear coefficient of thermal expansion
Across Flow
ISO 11359-2
1 E-4/℃
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1540 kg/m
Shrinkage rate
Across Flow
ISO 294-4
0.3-0.5 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Compared to the Leakage Traceability Index (CTI)
IEC 60112
425
Volume resistivity
100Hz
IEC 60250
4.5
Volume resistivity
1MHz
IEC 60250
4.1
Dielectric dissipation factor
100Hz
IEC 60250
22 E-4
Dielectric dissipation factor
1MHz
IEC 60250
160 E-4
Volume resistivity
IE 60093
>1E13 ohm.m
Surface resistivity
IEC 60093
>1E15 Ohm
Dielectric strength
IEC 60243-1
31 KV/mm