برگه داده فنی مقایسهOther performance شرایط آزمون روش آزمون نتیجه آزمون Glow wire combustion index (GWFI) 2.0mm IEC 695-2-1 960 °C Limiting Oxygen Index (LOI) ASTM D-2863 36 %
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 300℃/1.2kg ASTM D-1238 10 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Break ASTM D-638 59 Mpa Impact strength of cantilever beam gap 总能量@23℃ ASTM D-1822 631 KJ/m Rockwell hardness ASTM D-785 59 M Scale tensile strength Yield ASTM D-638 61 Mpa Bending modulus ASTM D-790 2330 Mpa bending strength ASTM D-790 98 Mpa elongation Break ASTM D-638 115 % Impact strength of cantilever beam gap 23℃ ASTM D-256 未破裂 Tensile modulus ASTM D-638 2380 Mpa Impact strength of cantilever beam gap 23℃ ASTM D-256 694 J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature 50℃/hr,50n重 ASTM D-1525 151 °C Hot deformation temperature Annealed@0.45MPa ASTM D-648 137 °C Shrinkage rate ASTM D-696 65×10 mm/mm/℃ Hot deformation temperature Unannealed@1.82MPa ASTM D-648 127 °C Ball indentation temperature IEC 598-1 >125 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.005-0.007 mm/mm
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Compared to the Leakage Traceability Index (CTI) 2.0mm IEC 112 225 V