Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 4800-10 STYRON TAIWAN
--
Electrical field,Electronic field
High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | STYRON TAIWAN/4800-10 |
|---|---|---|---|
| Limiting Oxygen Index (LOI) | ASTM D-2863 | 36 % | |
| Glow wire combustion index (GWFI) | 2.0mm | IEC 695-2-1 | 960 °C |
| Basic performance | Test Condition | Test Method | STYRON TAIWAN/4800-10 |
|---|---|---|---|
| melt mass-flow rate | 300℃/1.2kg | ASTM D-1238 | 10 g/10min |
| Mechanical properties | Test Condition | Test Method | STYRON TAIWAN/4800-10 |
|---|---|---|---|
| tensile strength | 断裂 | ASTM D-638 | 59 Mpa |
| 屈服 | ASTM D-638 | 61 Mpa | |
| elongation | 断裂 | ASTM D-638 | 115 % |
| Impact strength of cantilever beam gap | 总能量@23℃ | ASTM D-1822 | 631 KJ/m |
| Tensile modulus | ASTM D-638 | 2380 Mpa | |
| Rockwell hardness | ASTM D-785 | 59 M Scale | |
| Flexural modulus | ASTM D-790 | 2330 Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 未破裂 |
| bending strength | ASTM D-790 | 98 Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 694 J/m |
| Electrical performance | Test Condition | Test Method | STYRON TAIWAN/4800-10 |
|---|---|---|---|
| Compared to the Leakage Traceability Index (CTI) | 2.0mm | IEC 112 | 225 V |
| physical property | Test Condition | Test Method | STYRON TAIWAN/4800-10 |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.005-0.007 mm/mm |
| Thermal performance | Test Condition | Test Method | STYRON TAIWAN/4800-10 |
|---|---|---|---|
| Heat distortion temperature | 未退火@1.82MPa，HDT | ASTM D-648 | 127 °C |
| Shrinkage rate | ASTM D-696 | 65×10 mm/mm/℃ | |
| Ball indentation temperature | IEC 598-1 | ＞125 °C | |
| vicat | 50℃/小时，50n重 | ASTM D-1525 | 151 °C |
| Heat distortion temperature | 退火@0.45MPa，HDT | ASTM D-648 | 137 °C |