برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus 17000 tensile strength Yield 245 Tensile modulus ISO 527 17000 Mpa tensile strength Yield ISO 527 245 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break 2.6 bending strength 350 Bending modulus 15000 Charpy Notched Impact Strength 13 Charpy Notched Impact Strength 100 Melting temperature 260 Elongation at Break ISO 527 2.6 % bending strength ISO 178 350 Mpa Bending modulus ISO 178 15000 Mpa Charpy Notched Impact Strength ISO 179 13 kJ/m² Charpy Notched Impact Strength ISO 179 100 kJ/m² Melting temperature ISO 11357 260 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 0.5 Shrinkage rate Flow 0.1 Water absorption rate 23℃ 24hr 0.24 Water absorption rate 23°C,Saturation 3.8 Water absorption rate 23℃,50RH,Equilibrium 1.3 Shrinkage rate ISO 294 0.5 % Shrinkage rate Flow ISO 294 0.1 % Water absorption rate 23℃ 24hr ISO 62 0.24 % Water absorption rate 23°C,Saturation 内部测试方法 3.8 % Water absorption rate 23℃,50RH,Equilibrium 内部测试方法 1.3 %
flame retardant performance شرایط آزمون روش آزمون نتیجه آزمون Fire rating: Natural black 0.75mm HB Fire rating: Natural black 1.5mm HB Fire rating: natural black 3.0mm HB Fire rating: Natural black 0.75mm UL 94 HB Fire rating: Natural black 1.5mm UL 94 HB Fire rating: natural black 3.0mm UL 94 HB
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.