PPA 4050 NT000 SOLVAY SHANGHAI
Omnix® HPPA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SOLVAY SHANGHAI/4050 NT000 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527 | 245 Mpa |
| Tensile modulus | 17000 | ||
| tensile strength | 屈服 | 245 | |
| Tensile modulus | ISO 527 | 17000 Mpa |
| Flame retardant performance | Test Condition | Test Method | SOLVAY SHANGHAI/4050 NT000 |
|---|---|---|---|
| Fire rating: natural black 3.0mm | HB | ||
| Fire rating: Natural black 1.5mm | UL 94 | HB | |
| Fire rating: natural black 3.0mm | UL 94 | HB | |
| Fire rating: Natural black 0.75mm | UL 94 | HB | |
| Fire rating: Natural black 1.5mm | HB | ||
| Fire rating: Natural black 0.75mm | HB |
| physical property | Test Condition | Test Method | SOLVAY SHANGHAI/4050 NT000 |
|---|---|---|---|
| Shrinkage rate | 流动 | ISO 294 | 0.1 % |
| ISO 294 | 0.5 % | ||
| Water absorption rate | 23℃,50RH,平衡 | 1.3 | |
| 23℃ 24hr | ISO 62 | 0.24 % | |
| Shrinkage rate | 0.5 | ||
| Water absorption rate | 23°C,饱和 | 内部测试方法 | 3.8 % |
| 23℃,50RH,平衡 | 内部测试方法 | 1.3 % | |
| Shrinkage rate | 流动 | 0.1 | |
| Water absorption rate | 23℃ 24hr | 0.24 | |
| 23°C,饱和 | 3.8 |
| Thermal performance | Test Condition | Test Method | SOLVAY SHANGHAI/4050 NT000 |
|---|---|---|---|
| bending strength | ISO 178 | 350 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 100 kJ/m² | |
| elongation at break | 2.6 | ||
| melting temperature | ISO 11357 | 260 °C | |
| elongation at break | ISO 527 | 2.6 % | |
| melting temperature | 260 | ||
| Flexural modulus | ISO 178 | 15000 Mpa | |
| Charpy Notched Impact Strength | 100 | ||
| bending strength | 350 | ||
| Flexural modulus | 15000 |