برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 0.600mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D638 2560 Mpa tensile strength Yield ASTM D638 59.0 Mpa tensile strength Break ASTM D638 52.0 Mpa elongation Yield ASTM D638 5.7 % elongation Break ASTM D638 64 % Bending modulus 50.0mmSpan ASTM D790 2300 Mpa bending strength Yield,50.0mmSpan ASTM D790 91.0 Mpa bending strength Break,50.0mmSpan ASTM D790 90.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 124 °C Linear coefficient of thermal expansion MD:-40to40°C ASTME831 6.3E-05 cm/cm/°C Linear coefficient of thermal expansion TD:-40to40°C ASTME831 6.9E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 300°C/1.2kg ASTM D1238 12 g/10min Shrinkage rate MD:24hr ASTM D955 0.60-0.65 % Shrinkage rate TD:24hr ASTM D955 0.60-0.65 % Water absorption rate 24hr,50%RH ASTM D570 0.010 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Relative permittivity 1.00GHz IEC 60250 2.92 Dissipation factor 1.00GHz IEC 60250 7E-03
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.