PC DX11354 BKNAT SABIC INNOVATIVE NANSHA
LEXAN™
Electronic and Electrical Applications,Plastic bag,LDS
High impact resistance,UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354 BKNAT |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2560 Mpa | |
| elongation | 断裂 | ASTM D638 | 64 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 91.0 Mpa |
| elongation | 屈服 | ASTM D638 | 5.7 % |
| tensile strength | 断裂 | ASTM D638 | 52.0 Mpa |
| 屈服 | ASTM D638 | 59.0 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2300 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 90.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354 BKNAT |
|---|---|---|---|
| Dissipation Factor | 1.00GHz | IEC 60250 | 7E-03 |
| relative permittivity | 1.00GHz | IEC 60250 | 2.92 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354 BKNAT |
|---|---|---|---|
| UL flame retardant rating | 0.600mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354 BKNAT |
|---|---|---|---|
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.010 % |
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.60-0.65 % |
| MD:24小时 | ASTM D955 | 0.60-0.65 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354 BKNAT |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6.9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 124 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C |