برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون turbidity ASTM D1003 1.1 % transmissivity ASTM DI 003 90.2 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256 51 J/m Bending modulus 1.27mm/min ASTM D790 2090 Mpa bending strength 1.27mm/min ASTM D790 70.8 Mpa Elongation at Break 50mm/min ASTM D638 88 % elongation Yield,50mm/min ASTM D638 5.1 % tensile strength Break50mm/min ASTM D638 29.2 Mpa tensile strength Yield,50mmzmin ASTM D638 51 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature 10N ASTM D1525 79.1 °C Hot deformation temperature 1.8MPa ASTM D648 66.2 °C Hot deformation temperature 0.45MPa ASTM D648 76.2 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24hr在水里 ASTM D570 0.15 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dissipation factor ASTM DI 50 0.0246 Dissipation factor ASTM DI 50 0.0058 Dielectric constant ASTM D150 2.13 Dielectric constant ASTM DI50 2.32 Dielectric strength 2kV/s, 短期 ASTM D149 15.83 KV/mm Surface resistivity ASTM D257 10500000000000000 Ω Volume resistivity ASTM D257 1230000000000000 Ω.cm
hardness شرایط آزمون روش آزمون نتیجه آزمون Hardness (Rockwell R) ASTM D785 119