برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
elastomer شرایط آزمون روش آزمون نتیجه آزمون tensile strength 50%Strain ASTM D412 3.40 Mpa tear strength ASTM D624 76.0 kN/m Permanent compression deformation ASTM D395 49 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D638 14.0 Mpa elongation Break ASTM D638 820 % Bending modulus ASTM D790 23.0 Mpa Compressive modulus ASTM D695 2.40 Mpa Taber abraser 1000Cycles ASTM D1044 20.0 mg
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Brittle temperature ASTM D746 -65.0 °C Vicat softening temperature ASTM D1525 89.0 °C Melting temperature DSC 180 °C Linear coefficient of thermal expansion MD ASTM D696 2E-04 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 10 g/10min Shrinkage rate MD:2.00mm ASTM D955 0.40 % Water absorption rate Equilibrium,23°C,65%RH ASTM D570 0.56 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D257 1E+12 ohms·cm Dielectric strength ASTM D149 20 KV/mm
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreD ASTM D2240 31