برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength ASTM D638 69 Mpa Elongation at Break ASTM D638 60 % bending strength ASTM D790 103 Mpa Bending modulus ASTM D790 2940 Mpa Impact strength of cantilever beam gap ASTM D256 78 J/m Rockwell hardness ASTM D785 120 R Wear resistance ASTM D1044 13 tensile strength ASTM D638/ISO 527 69 kg/cm²(MPa)[Lb/in²] elongation ASTM D638/ISO 527 60 % Rockwell hardness ASTM D785 94 Bending modulus ASTM D790/ISO 178 2940 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 103 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238 10 g/10min Linear coefficient of thermal expansion 10 Hot deformation temperature 1.82MPa ASTM D648 136 °C Hot deformation temperature 0.45MPa ASTM D648 172 °C UL flame retardant rating UL 94 HB Combustibility (rate) UL 94 HB Hot deformation temperature HDT ASTM D648/ISO 75 136 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate ASTM D570 0.2 % Shrinkage rate Flow 1.8-2.2 % Shrinkage rate Across Flow 1.8-2.2 % density ASTM D792/ISO 1183 1.42 Water absorption rate ASTM D570/ISO 62 0.2 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.