POM 4010 ASAHI JAPAN
TENAC™
Household appliances、Automotive sector
High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/4010 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 103 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2940 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790 | 103 Mpa | |
| wear resistance | ASTM D1044 | 13 | |
| elongation | ASTM D638/ISO 527 | 60 % | |
| Rockwell hardness | ASTM D785 | 120 R | |
| Impact strength of cantilever beam gap | ASTM D256 | 78 J/m | |
| Rockwell hardness | ASTM D785 | 94 | |
| elongation at break | ASTM D638 | 60 % | |
| Flexural modulus | ASTM D790 | 2940 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 69 kg/cm²(MPa)[Lb/in²] | |
| ASTM D638 | 69 Mpa |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/4010 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.42 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/4010 |
|---|---|---|---|
| Shrinkage rate | 平行方向 | 1.8-2.2 % | |
| 垂直方向 | 1.8-2.2 % | ||
| Water absorption rate | ASTM D570 | 0.2 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/4010 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| melt mass-flow rate | ASTM D1238 | 10 g/10min | |
| Heat distortion temperature | 0.45MPa，HDT | ASTM D648 | 172 °C |
| HDT | ASTM D648/ISO 75 | 136 ℃（℉） | |
| 1.82MPa，HDT | ASTM D648 | 136 °C | |
| Linear coefficient of thermal expansion | 10 | ||
| UL flame retardant rating | UL 94 | HB |