برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون characteristic PA66.30%玻纤增强.热稳定.高耐摩擦磨损
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength (Dry) ISO 180 70.0 kJ/m² Impact strength of cantilever beam gap (Dry) ISO 180 13.0 kJ/m² Tensile stress (Dry),Break ISO 527-1 185 Mpa Tensile strain (Dry),Break ISO 527-1 2.8 % Tensile modulus (Dry) ISO 527-1 10300 Mpa Bending modulus (Dry) ISO 178 9200 Mpa bending strength (Dry) ISO 178 270 Mpa Charpy Notched Impact Strength (Dry) ISO 179 11.0 kJ/m² Charpy Notched Impact Strength ASTM D256/ISO 179 13 kg·cm/cm(J/M)ft·lb/in Charpy Notched Impact Strength ASTM D256/ISO 179 80 kg·cm/cm(J/M)ft·lb/in Elongation at Break ASTM D638/ISO 527 2.8 % Tensile modulus ASTM D638/ISO 527 10300 kg/cm²(MPa)[Lb/in²] tensile strength ASTM D638/ISO 527 185 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 9200 kg·cm/cm(J/M)ft·lb/in bending strength ASTM D790/ISO 178 270 kg·cm/cm(J/M)ft·lb/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature (Dry) ISO 3146 263 °C Hot deformation temperature 1.80 Mpa,Unannealed(Dry) ISO 75A-1 250 °C Hot deformation temperature HDT ASTM D648/ISO 75 250 ℃(℉) Melting temperature 263 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate (Dry),(Flow) ISO 294-4 0.30 % density ASTM D792/ISO 1183 1.50 Shrinkage rate ASTM D955 0.3-0.8 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.