Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 WRF403 NC010 DUPONT USA
Zytel®
sporting goods,Automotive Applications
Glass fiber reinforced,High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | DUPONT USA/WRF403 NC010 |
|---|---|---|---|
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 250 ℃（℉） |
| 1.80 Mpa，未退火(Dry) | ISO 75A-1 | 250 °C | |
| Melting temperature | 263 ℃（℉） | ||
| (Dry) | ISO 3146 | 263 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/WRF403 NC010 |
|---|---|---|---|
| Bending modulus | (Dry) | ISO 178 | 9200 Mpa |
| ASTM D790/ISO 178 | 9200 kg·cm/cm(J/M)ft·lb/in | ||
| bending strength | (Dry) | ISO 178 | 270 Mpa |
| ASTM D790/ISO 178 | 270 kg·cm/cm(J/M)ft·lb/in | ||
| Charpy Notched Impact Strength | (Dry) | ISO 179 | 11.0 kJ/m² |
| ASTM D256/ISO 179 | 80 kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at Break | ASTM D638/ISO 527 | 2.8 % | |
| Impact strength of cantilever beam gap | (Dry) | ISO 180 | 13.0 kJ/m² |
| Suspended wall beam without notch impact strength | (Dry) | ISO 180 | 70.0 kJ/m² |
| Tensile modulus | ASTM D638/ISO 527 | 10300 kg/cm²(MPa)[Lb/in²] | |
| (Dry) | ISO 527-1 | 10300 Mpa | |
| Tensile strain | (Dry)，断裂 | ISO 527-1 | 2.8 % |
| tensile strength | ASTM D638/ISO 527 | 185 kg/cm²(MPa)[Lb/in²] | |
| Tensile stress | (Dry)，断裂 | ISO 527-1 | 185 Mpa |
| other | Test Condition | Test Method | DUPONT USA/WRF403 NC010 |
|---|---|---|---|
| characteristic | PA66.30％玻纤增强.热稳定.高耐摩擦磨损 |
| Physical properties | Test Condition | Test Method | DUPONT USA/WRF403 NC010 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.50 | |
| Shrinkage rate | (Dry)，（Flow） | ISO 294-4 | 0.30 % |
| ASTM D955 | 0.3-0.8 % |