برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C, 3.20 mm, Injection ASTM D256 270 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 0.75 mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield, 23°C, 3.20 mm, Injection ASTM D638 53.9 Mpa elongation Break, 23°C, 3.20 mm, Injection ASTM D638 15 % Bending modulus 23°C, 3.20 mm, Injection ASTM D790 3330 Mpa bending strength 23°C, 3.20 mm, Injection ASTM D790 98.1 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 100 to 120 °C drying time 3.0 to 5.0 hr Suggested maximum moisture content 0.020 % Minimum Moisture Content 0.020 % Temperature at the rear of the barrel 280 to 295 °C Temperature in the middle of the barrel 285 to 300 °C Temperature at the front of the material cylinder 290 to 305 °C Spray nozzle temperature 290 to 305 °C Processing (melt) temperature 295 to 310 °C Mold temperature 90 to 110 °C Back pressure 0.981 to 3.92 Mpa Screw speed 40 to 70 rpm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm, Injection ASTM D648 137 °C RTI Elec UL 746 80.0 °C RTI Imp UL 746 80.0 °C RTI UL 746 80.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.25 g/cm³ melt mass-flow rate 300°C/1.2 kg ASTM D1238 9.0 g/10 min Shrinkage rate 23°C, 3.20 mm, Injection,Flow ASTM D955 0.20 - 0.40 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale, 23°C, Injection ASTM D785 124