physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD：24小时	ASTM D955	0.30 %
	Shrinkage rate	TD：24hr	ASTM D955	0.60 %
		Shrinkage rate	TD:24小时	ISO 294-4	0.60 %
		Shrinkage rate	Shrinkage rate	MD:24小时	ISO 294-4	0.33 %
Water absorption rate	24hr,50%RH	ASTM D570	0.17 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.23 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	32 kJ/m²
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	8.60 J
Multi axis Instrumented Impact Energy		ISO 6603-2	2.65 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	21 kJ/m²

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	断裂	ASTM D638	113 Mpa
tensile strength	tensile strength	断裂	ISO 527-2	113 Mpa
elongation	断裂	ASTM D638	2.2 %
Tensile strain	断裂	ISO 527-2	2.2 %
Flexural modulus		ASTM D790	7520 Mpa
Flexural modulus	Flexural modulus		ISO 178	7950 Mpa
bending strength		ASTM D790	179 Mpa
bending strength	bending strength		ISO 178	181 Mpa
Tensile modulus		ASTM D638	7580 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	7400 Mpa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	203 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火,64.0mm跨距，HDT	ISO 75-2/Af	204 °C